Product details
Technical filament from polyamide modified for 3D-printing in FFF.
Material shows nearly similar strength for injection-molded or printed parts by the good layer adhesion with highly reduced warping behaviour.
Recommended for all high strength parts with good heat- and media resistance.
The material can be used as a baseline for comparison of the fiber addition impact or where fibers or conductivity is not wanted in the printed part.
The material differs from PA PureLite by less heat absorption in the melting process and a lightly increased moisture sensitivity.
| Density | g/ cm³ | 1,2 |
| Modulus of Elasticity printed specimen | MPa (N/mm²) | 3400 |
| Tensile strength printed specimen x-y (+ 45°/-45°) | MPa (N/mm²) | 80 |
| Tensile strength printed specimen x-y (0°) | MPa (N/mm²) | 80 |
| Tensile strength printed specimen x-y (90°) | MPa (N/mm²) | 30 |
| Tensile stress printed specimen x-y (0°) | MPa (N/mm²) | 77,31 |
| Elongation printed specimen (0°) | % | 3,56 |
| Flexural modulus printed specimen (+ 45°/-45°) | GPa (kN/mm²) | 2,37 |
| Impact strength printed specimen x-y (+ 45°/-45°)(Charpy) | kJ/m² | — |
| Shore hardness | — | — |
| Glass transition temp. | °C | 72 |
| Heat distortion temp.(HDT) | °C | 90 |
You might also like
Specialist retailer of 3D Printers, 3D Scanners and 3D Software since 2013
My Account
We accept
Categories
CUSTOMER REVIEWS
© Copyright - Dream 3D Ltd | Cookie Policy | Privacy Policy | Price Match Promise | Refunds/Returns/Cancellations Policy
Contact us for a quote